C95500铜合金【铝青铜C95500产品简介】
******************************************
镍铝青铜,其独特的综合性能的高强度,良好的疲劳,优良的耐腐蚀性能在海水中,非引发和磨损特性使其成为一个受欢迎的选择整个光谱的行业。
它有非常高的抗磨损性能运行时对大多数等级的钢和世界基础上用于航空航天起落架灌木和轴承,其强度、疲劳、耐磨性、耐冲击性和耐蚀性证明。
化学成分表：
|
Element |
Cu |
Al |
Ni+Co |
Fe |
Mn |
Si |
Sn |
Zn |
|
% |
Bal |
9.0-11.0 |
4.0-5.5 |
2.0-4.0 |
1.5max |
0.25max |
0.2max |
0.3max |
机械性能表：
|
||||||||
|
Form |
Size Range |
Yield 0.2% |
UTS |
Elong % |
Hardness (HB) |
|||
|
Metric |
Imperial |
MPa |
Ksi |
MPa |
Ksi |
% |
(HB) |
|
|
020 |
75-300mm dia |
3- 12” dia |
300-350 |
43.5-50.7 |
600-700 |
87-101 |
12-21 |
180-240 |
|
HR50 |
50-80 mm dia |
2.0- 3.2” dia |
380-430 |
62.3-62.3 |
725-800 |
105-116 |
10-15 |
180-240 |
|
TQ50 |
80-130 mm dia |
3.2 – 5.1” dia |
320- 400 |
46.4-58.0 |
620-770 |
90-111.7 |
15-20 |
180-240 |
020 –Hot forged and annealed, HR50 Drawn and Stress relieved (High Strength) TQ50 Quench hardened and temper annealed.
物理性质AMS 4640
密度- 0.274磅/ in3在68 F
特定的重力- 7.58
电阻率- 116.0 ohms-cmil /英尺@ 68 F
导电率- 7% IACS @ 68 F
镍铝青铜的典型使用AMS 4640
-阀茎、泵轴、密封腺体,防喷器部分
,起落架衬套及轴承、皮瓣衬套,致动器,部分,支撑套管
汽车气门,气门座
其他工业——球、齿轮、凸轮、轴系、发电站的冷凝器管和脱盐装置,气门座,气门,泵轴、结构成员,、热交换器、头,换热器法兰、轴承、轴套、阀球,液压衬套为地球移动设备、耐腐蚀的文章,飞机零件、焊接管
它们是QAl5、QAl7、QAl9-2、QAl9-4、QAl9-5-1-1、QAl10-3-1.5、QAl10-4-4、QAl10-5-5、QAl11-6-6.而美国ASTM标准中加工铝青铜共有26，铸造合金有18个。铝青铜的基本合金组成为Cu-Al、Cu-Al-Fe、Cu-Al-Ni、Cu-Al-Fe-Ni、Cu-Al-Fe-Ni-Mn等。
公司常年备现货库存。欢迎各界人士莅临参观指导！！！
UNS No. C95200; UNS No. CuAl10Fe5Ni5-C; UNS No. CuAl10Fe5Ni5-C; UNS No. C95410; UNS No. C95500; UNS No. CuAl10Fe5Ni5-C; UNS No. C95600; UNS No. C95700; UNS No. CuAl10Fe5Ni5-C; UNS No. C95820; and UNS No. C95900.
(In Tension)
|
Imperial |
Metric |
|
|
Density |
0.274lb/in³ @ 68º F |
7580 kg/m³ @ 20ºC |
|
Specific Gravity |
7.58 |
7.58 |
|
Specific Heat |
0.090 Btu/lb º F @68º F |
376.7 J/kg ºC @20 ºC |
|
Electrical Conductivity |
7% IACS @ 68º F |
0.041mega Siemens/cm @20 ºC |
|
Thermal Conductivity |
22.6 Btu.ft(hr.ft² º F) @68º F |
0.391W/cm ºC @20 ºC |
|
Thermal Expansion |
9.0 x10ˉ 6 per º F (68-572 º F ) |
15.5 x10ˉ 6 perºC (20-300 ºC) |
|
Electrical Resistivity |
116Ω-cmil/ft @ 68º F |
19.28 µ Ω-cm@20 ºC |
|
Relative Magnetic Permeability |
1.4µ |
|
|
Machining Index |
20 (Based on free machining brass 100%) |
|
|
Modulus of Rigidity |
6800ksi |
46884MPa |
|
Modulus of Elasticity |
18200ksi |
125484MPa |
|
Melting Range |
1920-1960 ºF |
1049-1071ºC |
|
Hot Working Range |
1450-1700 ºF |
788-927 ºC |
|
Cold Working |
Limited |
|
|
Cryogenic |
Retains properties down to – 302 ºF |
(-190 ºC) |
|
Elevated Temperatures |
Retains properties to 662 ºF |
(350 ºC) |